Presented in this report are the results of stress corrosion cracking testing per ASTM G36 (Standard Practice for Performing Stress-Corrosion Cracking Tests in a. austenitic stainless steel was studied in accordance with the ASTM G The samples were unidirectional cold-rolled up to 60 and 90 percent reduction in. Revised ASTM G36 apparatus. This client had been testing stress corrosion- cracking in metal welds by clamping a QVF 2″ glass pipe fitting to his samples.

Author: Zugal Meztishicage
Country: Chad
Language: English (Spanish)
Genre: Spiritual
Published (Last): 20 May 2012
Pages: 380
PDF File Size: 16.1 Mb
ePub File Size: 6.21 Mb
ISBN: 958-2-38206-446-3
Downloads: 68864
Price: Free* [*Free Regsitration Required]
Uploader: Faujinn

Crack characteristics were investigated by preparing metallographic sections of the test specimens. Link to Active This link will always route to the current Asfm version of the standard. Corrosion Testing Laboratories, Inc. Two 2 1-foot long pieces of 0.

Deepest crack found on longitudinal cross-section of bare ashm. Materials that normally provide acceptable resistance in hot chloride service may crack in this test.

Test procedures conformed to the referenced ASTM test method. It was decided that cracks in the bare astj could be best examined using a longitudinal cross-section, while the cracks in the finned tube could be best examined using a transverse cross-section.

Link to Active This link will always route to the current Active version of the standard. Return to Corrosion Testing. Historical Version s – view previous versions of standard.

See Section 7 for specific safety precautions. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. The test specimens were immersed in the boiling solution and supported using the suggested ladder-back cradles.

The boiling points of aqueous magnesium chloride solutions at one atmosphere pressure as a function of concentration are shown graphically in Fig. Circumferential cracks with connecting longitudinal crack in base metal of bare tube.

Related Files:  C5706 DATASHEET EBOOK

The test may not be relevant to stress-corrosion cracking in polythionic acid or caustic environments. Accompanying paperwork states that both types of tube were fabricated from the same heat adtm of material.

Newark, Delaware USA It is the responsibility of the user asttm this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. The weld and HAZ of the finned tube appeared to have more cracks than the base metal, and the cracks appear to nearly connect from fin to fin.

CTL-ASTM G36 – STRESS CORROSION CRACKING in a BOILING MAGNESIUM CHLORIDE SOLUTION

Deepest cracks found on transverse cross-section of qstm tube. Regular examination periods for test specimen cracking were scheduled. Microphotographs of the deepest cracks found on the mounted sections are shown in Figures 3 and 4.

The boiling astmm of aqueous magnesium chloride solutions at one atmosphere pressure as a function of concentration are shown graphically in Fig. Although this test may be performed using various concentrations of magnesium chloride, this procedure covers a test solution held at a constant boiling temperature of No preparation other than deburring and degreasing was performed on the test specimens prior to testing. It is a method for g366 the effects of composition, heat treatment, surface finish, microstructure, and stress on the susceptibility of these materials to chloride stress corrosion cracking.

Etching both sections did not reveal any additional crack depth as sometimes occurs in metallographic studies of stress-corrosion cracking. Active view current version of standard. Black lines indicate the approximate location of the outer surface of the tube.

Related Files:  COMPUTER ORGANISATION AND ARCHITECTURE BY MORRIS MANO EPUB

On the finned test specimen, cracks extended down the fins from the outer edge to the tube wall in a direction roughly normal to the tube wall; at the tube wall the cracks extended in a short arc both longitudinally and circumferentially, the arcs stopping before the next fin was encountered.

Both test specimens were taken off test at 8 hours for examination at low ast.

G2MT Laboratories

Quality Assurance Return to Corrosion Testing. Circumferential cracking of the bare tube test specimen was apparent within the first 8 hours of testing even while the test specimen was on test. Careful examination is recommended for correct diagnosis of the cause of failure. Although this test may be performed using various concentrations of magnesium chloride, this procedure covers a test solution held at a constant boiling temperature of A suggested test apparatus capable of maintaining solution concentration and temperature within the prescribed limits for extended periods of time is also described herein.

Cracking of both test specimens was observed, and the tests were terminated. This zstm to the possibility of confusing stress-corrosion failures with mechanical failures induced by corrosion-reduced net cross sections.

Photographs of typical appearance of the cracks on both tubes are shown in Figures 1 and 2. This danger asfm particularly great when small cross section samples, high applied stress levels, long exposure periods, stress-corrosion resistant alloys, or a combination thereof are being used.

It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.